CHEMICAL SPECIFICATION REPORT FOR RAMMING MASS SiO2 97% Min. Grain Size Range 0-5 mm Maximum Recommended Use Limit 1700˚C / 3274˚F The achievement of perfection …
WhatsApp: +86 18221755073
typical specification sheet product :- silica ramming mass-premix grade ;- super grade sb-rm-p form :- granuler powder mix analysis- a) pysical b) chemical 1. appearance: super white 1. …
WhatsApp: +86 18221755073
Ramming mass is a refractory material used in high temperature environment. It is widely used in high temperature furnace lining construction in metallurgy, building materials, chemical industry, power industry and other industries. Its main components are refractory aggregate, binder and admixture.
WhatsApp: +86 18221755073
CHEMICAL SPECIFICATION REPORT FOR RAMMING MASS SiO2 97% Min. Grain Size Range 0-5 mm Maximum Recommended Use Limit 1700˚C / 3274˚F The achievement of perfection in quality is our Goal; but excellence isguarantee..
WhatsApp: +86 18221755073
Acidic Ramming Mass, also known as Silica Ramming Mass or Mix, is used in Coreless Induction Furnaces, for melting of scrap. High performance Silica Ramming Mixes (also known as Acidic Ramming Mass in generic terms), designed to minimize erosion in induction melting.
WhatsApp: +86 18221755073
Ramming mass acts as a protective barrier, resisting erosion and chemical attack from molten metal, slag, and other harsh substances. This erosion resistance extends the lifespan of furnace linings, reducing downtime and maintenance costs.
WhatsApp: +86 18221755073
Ramming mass is a refractory material used in high temperature environment. It is widely used in high temperature furnace lining construction in metallurgy, building materials, …
WhatsApp: +86 18221755073
By understanding the three types of ramming masses, industries can make the right choices to optimize their applications. Proper selection can enhance operational efficiency, reduce maintenance costs, and improve …
WhatsApp: +86 18221755073
Ramming mix is characterized by thermal stability, corrosion resistance and wear resistance because it contains less binders, fire clay and moisture compared to plastic refractories. …
WhatsApp: +86 18221755073
By understanding the three types of ramming masses, industries can make the right choices to optimize their applications. Proper selection can enhance operational efficiency, reduce maintenance costs, and improve product quality in steel, iron, non-ferrous metal production, and other high-temperature environments.
WhatsApp: +86 18221755073
typical specification sheet product :- silica ramming mass-premix grade ;- super grade sb-rm-p form :- granuler powder mix analysis- a) pysical b) chemical 1. appearance: super white 1. sio2: 99.8 % +- 0.5 % 2. moisture : nil 2. al2o3: 0.02 % 3. melting : 1700° c 3 ...
WhatsApp: +86 18221755073
Ramming mix is characterized by thermal stability, corrosion resistance and wear resistance because it contains less binders, fire clay and moisture compared to plastic refractories. ecommended for lining the iron melting coreless induction furnace. Premixed with binder to customer's specifications. Maximum recommended use limit- 3274 (1700).
WhatsApp: +86 18221755073
Acidic Ramming Mass, also known as Silica Ramming Mass or Mix, is used in Coreless Induction Furnaces, for melting of scrap. High performance Silica Ramming Mixes (also known as Acidic Ramming Mass in generic terms), …
WhatsApp: +86 18221755073
parameters ; specification . 1 : product brand . ind ram m 85 : 2 . description : 85 % mgo ramming mass . 3 : max service temp, ˚c. 1750 : 4 . sintering temperature,˚c
WhatsApp: +86 18221755073
Ramming mass acts as a protective barrier, resisting erosion and chemical attack from molten metal, slag, and other harsh substances. This erosion resistance extends the lifespan ...
WhatsApp: +86 18221755073
Ramming mass is a pre-blended Dry vibratables refractory made from a selected mix of SILICA GRAINS. This blend of grains along with a binder, BORIC ACID forms the working lining in an Induction furnace
WhatsApp: +86 18221755073
350 MIN ; After heating at 1500˚C / 3 hours. 400 MIN . 12 ; PERMANENT LINEAR CHANGE, % After heating at 1100˚C / 3 hours. ± 0.20 MAX . After heating at 1500˚C / 3 hours